牌号

LEXAN 243R

品名

特性

内部脱模, 紫外线稳定, 阻燃性

用途

电器汽车领域的应用

原厂原包供应Lexan PC 243R物性表

熔体流动速率MFR：10.5。紫外稳定。改良的阻燃性能。内含脱模剂

SABIC沙伯基础创新Lexan PC 243R中英文物性表资料

SABIC Innovative Plastics Lexan® 243R PC The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
Material Notes:	LEXAN 243R is a medium viscosity multi purpose UV stabilized grade and contains release agent to ensure easy processing. This grade is UL94-V2 at 0.8 mm approved.

Physical Properties物理性质	Metric公制数据	English英制数据	Comments测试方法
Density密度	1.20 g/cc	0.0434 lb/in³	ISO 1183
Moisture Absorption at Equilibrium吸湿平衡	0.15 %	0.15 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation吸水率	0.35 % @Temperature 23.0 °C	0.35 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动	0.0050 – 0.0070 cm/cm	0.0050 – 0.0070 in/in	on tensile bar; SABIC Method
Melt Flow熔体流动速率	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties力学性能	Metric公制数据	English英制数据	Comments测试方法
Hardness,硬度 H358/30	95.0 MPa	13800 psi	ISO 2039-1
Tensile Strength at Break断裂拉伸强度	70.0 MPa	10200 psi	50 mm/min; ISO 527
Tensile Strength, Yield屈服拉伸强度	63.0 MPa	9140 psi	50 mm/min; ISO 527
Elongation at Break断裂伸长率	110 %	110 %	50 mm/min; ISO 527
Elongation at Yield屈服伸长率	6.0 %	6.0 %	50 mm/min; ISO 527
Tensile Modulus拉伸模量	2.35 GPa	341 ksi	1 mm/min; ISO 527
Flexural Yield Strength弯曲屈服强度	90.0 MPa	13100 psi	2 mm/min; ISO 178
Flexural Modulus弯曲弹性模量	2.30 GPa	334 ksi	2 mm/min; ISO 178
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)	12.0 kJ/m² @Temperature -30.0 °C	5.71 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
	70.0 kJ/m² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	80103; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80103; ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Edgew 80103 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80103 sp=62mm; ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击	1.40 J/cm² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	ISO 179/2C
	7.30 J/cm² @Temperature 23.0 °C	34.7 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗	10 @Load 1.00 kg	10 @Load 2.20 lb	CS-17; SABIC Method
Electrical Properties电性能	Metric公制数据	English英制数据	Comments测试方法
Volume Resistivity体积电阻率	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance表面电阻	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093
Dielectric Constant介电常数	2.7 @Frequency 1.00e+6 Hz	2.7 @Frequency 1.00e+6 Hz	IEC 60250
	2.7 @Frequency 50.0 – 60.0 Hz	2.7 @Frequency 50.0 – 60.0 Hz	IEC 60250
Dielectric Strength介电强度	15.0 kV/mm @Thickness 1.00 mm	381 kV/in @Thickness 0.0394 in	short time; IEC 60243-1
	17.0 kV/mm @Thickness 3.20 mm	432 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor耗散因数	0.0010 @Frequency 50.0 – 60.0 Hz	0.0010 @Frequency 50.0 – 60.0 Hz	IEC 60250
	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	IEC 60250
Thermal Properties热性能	Metric公制数据	English英制数据	Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数	70.0 µm/m-°C @Temperature 23.0 – 80.0 °C	38.9 µin/in-°F @Temperature 73.4 – 176 °F	ISO 11359-2
Thermal Conductivity导热系数	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at热变形温度 0.46 MPa (66 psi)	136 °C	277 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at热变形温度 1.8 MPa (264 psi)	125 °C	257 °F	Edgew 120104 sp=100mm; ISO 75/Ae
Vicat Softening Point维卡软化点	141 °C	286 °F	Rate B/50; ISO 306
	142 °C	288 °F	Rate B/120; ISO 306
	153 °C	307 °F	Rate A/50; ISO 306
UL RTI, Electrical相对温度指数	130 °C	266 °F	UL 746B
UL RTI, Mechanical with Impact机械冲击热指数	125 °C	257 °F	UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数	125 °C	257 °F	UL 746B
Flammability, UL94阻燃等级	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in	UL 94
	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in	UL 94
Oxygen Index氧指数	25 %	25 %	LOI; ISO 4589
Glow Wire Test灼热丝测试	850 °C @Thickness 1.00 mm	1560 °F @Thickness 0.0394 in	Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties光学性质	Metric公制数据	English英制数据	Comments测试方法
Refractive Index折射率	1.586	1.586	ISO 489
Haze雾度	<= 0.80 % @Thickness 2.54 mm	<= 0.80 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible透光率	88 – 90 % @Thickness 2.54 mm	88 – 90 % @Thickness 0.100 in	ASTM D 1003

　以下是沙特-SABIC塑料LEXAN PC 243R物性表参数

V i s i t W 3 S ch o o l s . c o m!
V i s i t W 3 S ch o o l s . c o m!

Delivery ways
By Express 1KG-100KG
By Air 100KG-500KG
By Sea >500KG
By Express(FEDEX, UPS, DHL, TNT, EMS, etc...)
---Advantage: Fast ( takes about 7 -10 days in the delivery )by door to door service ---Disadvantage: expensive By Air Transportation
---Advantage: Fast ( takes about 8 - 12 days ) and cheaper than Express. ---Disadvantage: Customer need to take the goods from the airport. By Sea( Ocean ) Transportation
---Advantage: Much cheaper than Express or Air transportation.
--- Disadvantage: Slow and customer need to take the goods from the destination port.

国内运输：
1-100公斤，快递运送。
100-1000公斤，物流托运。
1000公斤以上，专车送货。
国际运输：
1-100公斤，快递运送。
100-1000公斤，海运，陆运，铁运，联运。
1000公斤以上，海运，陆运，铁运，联运。

We highly recommend shipping plastic resin by sea! Because it can reduce a lot of costs. Our customers usually arrange orders and shipping 30 days in advance.

LEXAN 243RPC内部脱模紫外线稳定阻燃性

Click to enlarge

Previous product

Best LEXAN 923X ¥1.00

Back to products

Next product

Best LEXAN LUX2614G ¥1.00

牌号	LEXAN 243R
品名	PC
特性	内部脱模, 紫外线稳定, 阻燃性
用途	电器汽车领域的应用

Compare

Add to wishlist

Categories: 沙特-SABIC, 沙特-SABIC Lexan PC

Description
Reviews (0)
送货方式

Description

SABIC Innovative Plastics Lexan® 243R PC The property table is provided by www.plas-cn.com, welcome to download, reprint please indicate the source!
Material Notes:	LEXAN 243R is a medium viscosity multi purpose UV stabilized grade and contains release agent to ensure easy processing. This grade is UL94-V2 at 0.8 mm approved.

Physical Properties物理性质	Metric公制数据	English英制数据	Comments测试方法
Density密度	1.20 g/cc	0.0434 lb/in³	ISO 1183
Moisture Absorption at Equilibrium吸湿平衡	0.15 %	0.15 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation吸水率	0.35 % @Temperature 23.0 °C	0.35 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow线性收缩率/流动	0.0050 – 0.0070 cm/cm	0.0050 – 0.0070 in/in	on tensile bar; SABIC Method
Melt Flow熔体流动速率	12 g/10 min @Load 1.20 kg, Temperature 300 °C	12 g/10 min @Load 2.65 lb, Temperature 572 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties力学性能	Metric公制数据	English英制数据	Comments测试方法
Hardness,硬度 H358/30	95.0 MPa	13800 psi	ISO 2039-1
Tensile Strength at Break断裂拉伸强度	70.0 MPa	10200 psi	50 mm/min; ISO 527
Tensile Strength, Yield屈服拉伸强度	63.0 MPa	9140 psi	50 mm/min; ISO 527
Elongation at Break断裂伸长率	110 %	110 %	50 mm/min; ISO 527
Elongation at Yield屈服伸长率	6.0 %	6.0 %	50 mm/min; ISO 527
Tensile Modulus拉伸模量	2.35 GPa	341 ksi	1 mm/min; ISO 527
Flexural Yield Strength弯曲屈服强度	90.0 MPa	13100 psi	2 mm/min; ISO 178
Flexural Modulus弯曲弹性模量	2.30 GPa	334 ksi	2 mm/min; ISO 178
Izod Impact, Notched悬臂梁缺口冲击强度 (ISO)	12.0 kJ/m² @Temperature -30.0 °C	5.71 ft-lb/in² @Temperature -22.0 °F	80103; ISO 180/1A
	70.0 kJ/m² @Temperature 23.0 °C	33.3 ft-lb/in² @Temperature 73.4 °F	80103; ISO 180/1A
Izod Impact, Unnotched悬臂梁无缺口冲击强度 (ISO)	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	80103; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80103; ISO 180/1U
Charpy Impact Unnotched夏比缺口试样冲击	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	Edgew 80103 sp=62mm; ISO 179/1eU
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	Edgew 80103 sp=62mm; ISO 179/1eU
Charpy Impact, Notched夏比缺口冲击	1.40 J/cm² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
	3.50 J/cm² @Temperature 23.0 °C	16.7 ft-lb/in² @Temperature 73.4 °F	ISO 179/2C
	7.30 J/cm² @Temperature 23.0 °C	34.7 ft-lb/in² @Temperature 73.4 °F	V-notch Edgew 80103 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles周期泰伯磨耗	10 @Load 1.00 kg	10 @Load 2.20 lb	CS-17; SABIC Method
Electrical Properties电性能	Metric公制数据	English英制数据	Comments测试方法
Volume Resistivity体积电阻率	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance表面电阻	>= 1.00e+15 ohm	>= 1.00e+15 ohm	ROA; IEC 60093
Dielectric Constant介电常数	2.7 @Frequency 1.00e+6 Hz	2.7 @Frequency 1.00e+6 Hz	IEC 60250
	2.7 @Frequency 50.0 – 60.0 Hz	2.7 @Frequency 50.0 – 60.0 Hz	IEC 60250
Dielectric Strength介电强度	15.0 kV/mm @Thickness 1.00 mm	381 kV/in @Thickness 0.0394 in	short time; IEC 60243-1
	17.0 kV/mm @Thickness 3.20 mm	432 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor耗散因数	0.0010 @Frequency 50.0 – 60.0 Hz	0.0010 @Frequency 50.0 – 60.0 Hz	IEC 60250
	0.010 @Frequency 1.00e+6 Hz	0.010 @Frequency 1.00e+6 Hz	IEC 60250
Thermal Properties热性能	Metric公制数据	English英制数据	Comments测试方法
CTE, linear, Parallel to Flow线性热膨胀系数	70.0 µm/m-°C @Temperature 23.0 – 80.0 °C	38.9 µin/in-°F @Temperature 73.4 – 176 °F	ISO 11359-2
Thermal Conductivity导热系数	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ISO 8302
Deflection Temperature at热变形温度 0.46 MPa (66 psi)	136 °C	277 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at热变形温度 1.8 MPa (264 psi)	125 °C	257 °F	Edgew 120104 sp=100mm; ISO 75/Ae
Vicat Softening Point维卡软化点	141 °C	286 °F	Rate B/50; ISO 306
	142 °C	288 °F	Rate B/120; ISO 306
	153 °C	307 °F	Rate A/50; ISO 306
UL RTI, Electrical相对温度指数	130 °C	266 °F	UL 746B
UL RTI, Mechanical with Impact机械冲击热指数	125 °C	257 °F	UL 746B
UL RTI, Mechanical without Impact无机械冲击热指数	125 °C	257 °F	UL 746B
Flammability, UL94阻燃等级	V-2 @Thickness 0.750 mm	V-2 @Thickness 0.0295 in	UL 94
	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in	UL 94
Oxygen Index氧指数	25 %	25 %	LOI; ISO 4589
Glow Wire Test灼热丝测试	850 °C @Thickness 1.00 mm	1560 °F @Thickness 0.0394 in	Glow Wire Flammability Index; IEC 60695-2-12
Optical Properties光学性质	Metric公制数据	English英制数据	Comments测试方法
Refractive Index折射率	1.586	1.586	ISO 489
Haze雾度	<= 0.80 % @Thickness 2.54 mm	<= 0.80 % @Thickness 0.100 in	ASTM D 1003
Transmission, Visible透光率	88 – 90 % @Thickness 2.54 mm	88 – 90 % @Thickness 0.100 in	ASTM D 1003

Reviews (0)

Reviews

There are no reviews yet.

Be the first to review “Best LEXAN 243R”

You must be logged in to post a review.

送货方式

Specification	Chair	Armchair	Sofas
Height	37"	42"	42"
Width	26.5"	32.5"	142"
Depth	19.5"	22.5"	24.5"
Assembly Required	No	No	Yes
Packaging Type	Box	Box	Box
Package Weight	55 lbs.	64 lbs.	180 lbs.
Packaging Dimensions	27" x 26" x 39"	45" x 35" x 24"	46" x 142" x 25"

Best LEXAN 243R

计量单位：公斤
最小订单量：25公斤

LEXAN 243R

Reviews

We highly recommend shipping plastic resin by sea! Because it can reduce a lot of costs. Our customers usually arrange orders and shipping 30 days in advance.

免运费发货！

24/7 支持。

在线支付。

退换货保障

Best LEXAN 243R

计量单位：公斤 最小订单量：25公斤

Size and packaging guidelines

LEXAN 243R

Reviews

We highly recommend shipping plastic resin by sea! Because it can reduce a lot of costs. Our customers usually arrange orders and shipping 30 days in advance.

Related products

免运费发货！

24/7 支持。

在线支付。

退换货保障

Sign in

计量单位：公斤
最小订单量：25公斤